P.Q.Liu 1) and W.H.Wang 2) 1) Department of Materials Science and Engineering
,
Shenyang Architectural and Civil Engineering Institute
,
Shenyang 110015
,
China 2) Department of Airport
,
CAAC Eastnorth Management
,
Shenyang 110043
,
China
金属学报(英文版)
The properties of a new magnesium Oxychloride cement (MOC) material formed by silica fume uniformly mix in MOC paste was presents. The influence of silica fume on the water resistance and compressive strength of MOC paste was invesigated in this study. It is shown that when 30 weight percent of silica fume is added to the MOC paste, a high strength and water resisting new material with 112MPa compressive strength and 1 00 water resisting coefficient could by obtained.